DIN 1652-3 Grade 15CrNi6 냉간 인발 또는 박리 및 페라이트-펄라이트 구조로 처리

-100.0 °C

217GPa

20.0 °C

212GPa

100.0 °C

207 GPa

200.0 °C

199 GPa

300.0 °C

192 GPa

400.0 °C

184 GPa

500.0 °C

175GPa

600.0 °C

164GPa

-100.0 °C

1.05E-5 1/K

20.0 °C

1.15E-5 1/K

100.0 °C

1.21E-5 1/K

200.0 °C

1.27E-5 1/K

300.0 °C

1.32E-5 1/K

400.0 °C

1.36E-5 1/K

500.0 °C

1.4E-5 1/K

600.0 °C

1.44E-5 1/K

-100.0 °C

423J/(kg·K)

20.0 °C

461J/(kg·K)

100.0 °C

479J/(kg·K)

200.0 °C

499J/(kg·K)

300.0 °C

517J/(kg·K)

400.0 °C

536J/(kg·K)

500.0 °C

558J/(kg·K)

600.0 °C

587J/(kg·K)

-100.0 °C

31.9 W/(m·K)

20.0 °C

37.6 W/(m·K)

100.0 °C

39.3 W/(m·K)

200.0 °C

40.1 W/(m·K)

300.0 °C

39.6 W/(m·K)

400.0 °C

38.4 W/(m·K)

500.0 °C

36.7 W/(m·K)

600.0 °C

34.8 W/(m·K)

-100.0 °C

10.9mm²/초

20.0 °C

10.4mm²/초

100.0 °C

10.1mm²/s

200.0 °C

9.7mm²/s

300.0 °C

9mm²/s

400.0 °C

8.1mm²/s

500.0 °C

7.1mm²/s

600.0 °C

5.9mm²/s