AA 3003 알루미늄 합금은 대기 내식성이 매우 뛰어나고 중등도 강도를 갖춘 널리 사용되는 합금입니다. 알루미늄 합금 중 가공성이 양호하지만 열처리로 경화되지 않습니다. 다른 알루미늄 합금과 달리 기존 용접 공법으로 용접이 가능하며, 냉간/열간 가공성이 우수하고 1000 시리즈 알루미늄보다 전반적으로 기계적 특성이 우수합니다.
| 특성 | 값 | 조건 | 관련 표준 |
|---|---|---|---|
| 밀도 | 2.73 g/cm³ | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 특성 | 값 | 조건 | 관련 표준 | 비고 |
|---|---|---|---|---|
| 굽힘 피로 강도 | 60.0 MPa | H14 | AA Standards | |
| 탄성 계수 | 69.0 GPa | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| 브리넬 경도 | 40.0 | H14 | AA Standards | |
| 평면 변형 파괴 인성 | 22.0 - 35.0 MPa·√m | - | - | 단조 3000 시리즈 알루미늄 대표값 |
| 푸아송 비 | 0.33 | - | - | 단조 3000 시리즈 알루미늄 대표값 |
| 전단 계수 | 25.0 - 26.0 GPa | - | - | 단조 3000 시리즈 알루미늄 대표값 |
| 인장 강도 | 140.0 - 180.0 MPa | H14 | AA Standards, ASTM B209, ASTM B313, ASTM B316, ASTM B547 | |
| 인장 강도 | 140.0 MPa | H14 | AA Standards, ASTM B210, ASTM B211, ASTM B234, ASTM B483 | |
| 인장 강도 | 150.0 MPa | H14 | AA Standards |
| 특성 | 온도 | 값 | 조건 | 관련 표준 | 비고 |
|---|---|---|---|---|---|
| 열팽창 계수 | 20 °C | 2.32×10⁻⁵ 1/K | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| 열팽창 계수 | 100 °C | 2.32×10⁻⁵ 1/K | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| 융점 | - | 640.0 - 655.0 °C | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| 비열 용량 | - | 893.0 - 920.0 J/(kg·K) | - | - | 단조 3000 시리즈 알루미늄 대표값 |
| 열전도율 | - | 159.0 - 193.0 W/(m·K) | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 특성 | 값 | 조건 | 관련 표준 |
|---|---|---|---|
| 전기 전도도 | 24,000,000 - 29,000,000 S/m | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 전기 저항률 | 3.45×10⁻⁸ - 4.17×10⁻⁸ Ω·m | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 원소 | 함량 | 조건 | 관련 표준 |
|---|---|---|---|
| 구리 (Cu) | 0.05 - 0.2 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 철 (Fe) | 0.70 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 망간 (Mn) | 1.0 - 1.5 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 실리콘 (Si) | 0.6 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 아연 (Zn) | 0.1 % | H14 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| 특성 | 평가 |
|---|---|
| 브레이징 | 일반: 상용 공정 및 방법으로 가능 |
| 내식성 | 응력 부식 균열: 운전 및 실험실 시험에서 손상 없음, 전반적: 매우 우수, 산업/해수 분위기에서 무보호 사용 가능 |
| 일반 가공성 | 일반: O, H12 상태에서 부적합, H14, H16, H25에서 불량 |
| 가공성(성형성) | 일반: O, H12에서 양호, H14, H25에서 보통, H16, H18에서 불량 |
금속
AA 3003 알루미늄 합금은 대기 내식성이 매우 뛰어나고 중등도 강도를 갖춘 널리 사용되는 합금입니다. 알루미늄 합금 중 가공성이 양호하지만 열처리로 경화되지 않습니다. 다른 알루미늄 합금과 달리 기존 용접 공법으로 용접이 가능하며, 냉간/열간 가공성이 우수하고 1000 시리즈 알루미늄보다 전반적으로 기계적 특성이 우수합니다. 일반 특성 특성 값 조건 관련 표준 밀도 2.73 g/cm³ H16 AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B483,
AA 1100은 부드럽고 열처리로 경화되지 않는 저강도 합금으로, 뛰어난 내식성을 제공합니다. 알루미늄 99%, 구리 0.12%로 구성되어 상업적으로 구매 가능한 가장 순도 높은 알루미늄 합금 등급입니다. 물리적 특성 일반 특성 특성값조건관련 표준 밀도2.71 g/cm³H14AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547 기계적 특성 특성값조건관련 표준비고 굴곡 피로 강도50.0 MPaH14AA St