| 특성 | 값 | 조건 | 관련 규격 |
|---|---|---|---|
| 밀도 | 2.705 g/cm³ | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 특성 | 값 | 조건 | 관련 규격 | 비고 |
|---|---|---|---|---|
| 굽힘 피로 강도 | 20.0 MPa | O | AA Standards | |
| 탄성 계수 | 69.0 GPa | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
| 브리넬 경도 | 19.0 [-] | O | AA Standards | |
| 평면 변형 파괴 인성 | 22.0 - 35.0 MPa·√m | 단조 1000 시리즈 알루미늄의 일반적인 값 | ||
| 푸아송 비 | 0.33 [-] | 단조 1000 시리즈 알루미늄의 일반적인 값 | ||
| 전단 계수 | 25.9 GPa | 단조 1000 시리즈 알루미늄의 일반적인 값 | ||
| 인장 강도 | 55.0 - 95.0 MPa | O | AA Standards, ASTM B209 | |
| 55.0 MPa | O | AA Standards, ASTM B211 | ||
| 60.0 - 95.0 MPa | O | AA Standards, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | ||
| 70.0 MPa | O | AA Standards |
| 특성 | 온도 | 값 | 조건 | 관련 규격 | 비고 |
|---|---|---|---|---|---|
| 열팽창 계수 | 20 °C | 2.36e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
| 100 °C | 2.36e-05 1/K | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | ||
| 융점 | 645.0 - 655.0 °C | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | ||
| 비열 용량 | 900.0 - 963.0 J/(kg·K) | 단조 1000 시리즈 알루미늄의 일반적인 값 | |||
| 열전도율 | 230.0 - 234.0 W/(m·K) | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 특성 | 값 | 조건 | 관련 규격 |
|---|---|---|---|
| 전기 전도도 | 35,000,000.0 - 36,000,000.0 S/m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 전기 저항률 | 2.78e-08 - 2.86e-08 Ω·m | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 원소 | 함량 (%) | 조건 | 관련 규격 |
|---|---|---|---|
| 알루미늄 | 99.6 | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 구리 | 0.05 | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 철 | 0.35 | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 마그네슘 | 0.03 | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 망간 | 0.03 | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 실리콘 | 0.25 | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 티타늄 | 0.03 | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 바나듐 | 0.05 | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 아연 | 0.05 | O | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 특성 | 평가 |
|---|---|
| 납땜 | 일반: 상업적 공정 및 방법으로 가능 |
| 내식성 | 응력 부식 균열: 운전 및 실험실 테스트 중 손상 없음, 일반: 매우 좋음, 산업 또는 해수 대기에서 무방호 상태에서도 양호 |
| 일반 가공성 | 일반: 부적합(O, H12), 나쁨(H14, H16, H18) |
| 가공성 | 일반(조건): 좋음(O, H12, H14), 허용 가능(H16, H18) |
금속
개요 AA 7075는 아연을 주 합금 원소로 하는 7000번대 초고강도 알루미늄 합금으로, 우수한 응력 부식 균열 저항성과 뛰어난 강도-중량비를 자랑합니다. 항공우주 산업의 주력 소재로 도입 이래 널리 사용되어 왔으며, 영하 온도에서 강도가 더욱 증가하는 특징이 있습니다. 인성은 중간 수준입니다. 추가 서비스: 절단, 도면 가공 부품 공급 | 공급사: STEEL SCOUT (유통업체) | 최소 주문: 1개 물리적·기계적 특성 (T6 상태) 일반 특성 특성값조건관련 표준 밀도2.81 g/cm³T6AA
AA 6061은 우수한 표면 마감과 양극 산화 처리 능력을 갖춘 쉽게 구할 수 있는 합금입니다. 용접성과 납땜성이 뛰어나며 표면 마감이 우수합니다. 해수와 대기 조건에 대한 내식성이 있습니다. 열간 단조에 적합합니다. 일반 물성 물성 값 조건 관련 표준 밀도 2.7 g/cm³ O AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 기계적 물성 물성 값 조건 관련 표준 비고