AA 6061은 우수한 표면 마감과 양극 산화 처리 능력을 갖춘 쉽게 구할 수 있는 합금입니다. 용접성과 납땜성이 뛰어나며 표면 마감이 우수합니다. 해수와 대기 조건에 대한 내식성이 있습니다. 열간 단조에 적합합니다.
| 물성 | 값 | 조건 | 관련 표준 |
|---|---|---|---|
| 밀도 | 2.7 g/cm³ | O | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| 물성 | 값 | 조건 | 관련 표준 | 비고 |
|---|---|---|---|---|
| 굴곡 피로 강도 | 60.0 MPa | O | AA 표준 | |
| 탄성 계수 | 69.0 GPa | O | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | |
| 브리넬 경도 | 30.0 [-] | O | AA 표준 | |
| 평면 변형 파괴 인성 | 22.0 - 35.0 MPa·√m | 단조 6000 시리즈 알루미늄 대표값 | ||
| 푸아송 비 | 0.33 [-] | 단조 6000 시리즈 알루미늄 대표값 | ||
| 전단 계수 | 26.0 - 26.5 GPa | 단조 6000 시리즈 알루미늄 대표값 | ||
| 인장 강도 | 125.0 MPa | O | AA 표준 | |
| 인장 강도 | 150.0 MPa | O | AA 표준, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B483 | |
| 인장 강도 | 155.0 MPa | O | AA 표준, ASTM B211, ASTM B316 |
| 물성 | 온도 | 값 | 조건 | 관련 표준 | 비고 |
|---|---|---|---|---|---|
| 열팽창 계수 | 20 °C | 2.36e-05 1/K | O | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | |
| 열팽창 계수 | 100 °C | 2.36e-05 1/K | O | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | |
| 녹는점 | 580.0 - 650.0 °C | O | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 | ||
| 비열 용량 | 887.0 - 963.0 J/(kg·K) | 단조 6000 시리즈 알루미늄 대표값 | |||
| 열전도율 | 155.0 - 180.0 W/(m·K) | O | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| 물성 | 값 | 조건 | 관련 표준 |
|---|---|---|---|
| 전기 전도도 | 23000000.0 - 27000000.0 S/m | O | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| 전기 저항률 | 3.7e-08 - 4.35e-08 Ω·m | O | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| 원소 | 함량 | 조건 | 관련 표준 |
|---|---|---|---|
| 크로뮴 | 0.04 - 0.35 % | O | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| 구리 | 0.15 - 0.4 % | O | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| 철 | 0.70 % | O | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| 마그네슘 | 0.8 - 1.2 % | O | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| 망간 | 0.15 % | O | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| 실리콘 | 0.4 - 0.8 % | O | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| 티타늄 | 0.15 % | O | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| 아연 | 0.25 % | O | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 |
| 특성 | 평가 |
|---|---|
| 납땜 | 일반: 상용 공정 및 방법으로 가능 |
| 내식성 | 응력 부식 균열: 작동 및 실험실 테스트 중 손상 없음 (O, T6, T651, T652, T6510, T6511), 작동 중 손상 없음, 실험실 테스트에서 제한적 손상 (T4, T451, T4510, T4511), 일반: 양호, 산업 또는 해수 대기에서 무보호 상태에서도 양호 |
| 일반 가공성 | 일반: 불량(O), 충분(T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511) |
| 가공성 | 일반(조건): 양호(O), 허용(T4, T451, T4510, T4511), 불량(T6, T651, T652, T6510, T6511) |
금속
개요 알루미늄 합금 AA 2219는 구리 첨가제로 생산되는 시효경화형 합금입니다. 우수한 구조적 강도로 잘 알려져 있으며, 수많은 고온 응용 분야에 사용됩니다. 가공, 성형, 열처리, 냉간 가공 등 다양한 금속 가공 공정에 적합한 합금입니다. 특성 일반 특성 특성 값 조건 관련 표준 밀도 2.84 g/cm³ O AA Standards, ASTM B209, ASTM B221, ASTM B241 기계적 특성 특성 값 조건 관련 표준 비고 탄성 계수 73.0 GPa O AA Standards, ASTM
개요 AA 6061은 우수한 표면 마감과 양극 산화 처리 능력을 갖춘 널리 사용되는 알루미늄 합금입니다. 용접성과 납땜성이 뛰어나며 깨끗한 표면 마감을 제공합니다. 해수 및 대기 조건에 대한 내식성이 우수하며, 단조 가공에도 적합합니다. 물성 데이터 일반 특성 특성값조건관련 표준 밀도2.7 g/cm³T4AA 표준, ASTM B209, B210, B211, B221, B234, B241, B313, B345, B483, B547 기계적 특성 특성값조건관련 표준비고 굴곡 피로 강도95.0 MPaT4AA 표준 탄성