AA 2014 T6는 석출경화 열처리(T6)를 통해 2014 합금 중 가장 높은 강도를 구현한 소재입니다. 우수한 기계적 물성과 가공성을 겸비하여 고하중 구조용 부품에 적합합니다.
| 항목 | 값 | 조건 | 관련 표준 |
|---|---|---|---|
| 밀도 | 2.8 g/cm³ | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| 항목 | 값 | 조건 | 관련 표준 | 비고 |
|---|---|---|---|---|
| 굴곡 피로 강도 | 125.0 MPa | T6 | AA Standards | |
| 탄성 계수 | 73.0 GPa | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 | |
| 브리넬 경도 | 135.0 | T6 | AA Standards | |
| 평면 변형 파괴 인성 | 22.0 – 35.0 MPa·√m | – | – | 단조 2000계열 알루미늄 일반값 |
| 푸아송 비 | 0.33 | – | – | 단조 2000계열 알루미늄 일반값 |
| 전단 계수 | 26.0 – 27.5 GPa | – | – | 단조 2000계열 알루미늄 일반값 |
| 인장 강도 | 395.0 MPa | T6 | AA Standards, ASTM B247 | |
| 인장 강도 | 400.0 MPa | T6 | AA Standards, ASTM B247 | |
| 인장 강도 | 405.0 MPa | T6 | AA Standards, ASTM B209, ASTM B247 | |
| 인장 강도 | 415.0 MPa | T6 | AA Standards, ASTM B241, ASTM B247 | |
| 인장 강도 | 420.0 MPa | T6 | AA Standards, ASTM B247 | |
| 인장 강도 | 425.0 MPa | T6 | AA Standards, ASTM B247 | |
| 인장 강도 | 435.0 MPa | T6 | AA Standards, ASTM B209, ASTM B247 | |
| 인장 강도 | 440.0 MPa | T6 | AA Standards, ASTM B209, ASTM B241, ASTM B247 | |
| 인장 강도 | 450.0 MPa | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B247 | |
| 인장 강도 | 455.0 MPa | T6 | AA Standards, ASTM B209 | |
| 인장 강도 | 460.0 MPa | T6 | AA Standards, ASTM B209 | |
| 인장 강도 | 470.0 MPa | T6 | AA Standards, ASTM B241 | |
| 인장 강도 | 485.0 MPa | T6 | AA Standards |
| 항목 | 온도 | 값 | 조건 | 관련 표준 | 비고 |
|---|---|---|---|---|---|
| 열팽창 계수 | 20 °C | 2.3×10⁻⁵ 1/K | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 | |
| 열팽창 계수 | 100 °C | 2.3×10⁻⁵ 1/K | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 | |
| 융점 | – | 505.0 – 635.0 °C | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 | |
| 비열 용량 | – | 816.0 – 963.0 J/(kg·K) | – | – | 단조 2000계열 알루미늄 일반값 |
| 열전도율 | – | 134.0 – 193.0 W/(m·K) | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| 항목 | 값 | 조건 | 관련 표준 |
|---|---|---|---|
| 전기 전도도 | 20,000,000 – 29,000,000 S/m | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| 전기 저항률 | 3.45×10⁻⁸ – 5.0×10⁻⁸ Ω·m | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| 원소 | 함량 | 조건 | 관련 표준 |
|---|---|---|---|
| 크로뮴 (Cr) | 0.1 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| 구리 (Cu) | 3.9 – 5.0 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| 철 (Fe) | 0.70 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| 마그네슘 (Mg) | 0.2 – 0.8 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| 망간 (Mn) | 0.4 – 1.2 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| 실리콘 (Si) | 0.5 – 1.2 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| 티타늄 (Ti) | 0.15 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| 아연 (Zn) | 0.25 % | T6 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| 항목 | 평가 |
|---|---|
| 납땜성 | 일반: 알려진 납땜 공법 없음 |
| 내식성 | 응력 부식 균열: 인장 응력이 결정 입계에 수직인 영역에서 작동 손상 발생, 실험실 시편에서는 제한적 손상, 전반적으로 양호하나 원칙적으로 보호 필요 |
| 일반 가공성 | 일반: 열처리 상태 O에서는 불량, 그 외 양호~허용 수준 |
| 성형성 | 일반 (조건): T3, T4, T451에서 불량, T6, T651, T6510, T6511에서는 부적합 |
금속
개요 AA 2014는 강도, 가공성, 용접성을 겸비한 알루미늄 합금으로, 열처리 후에도 강도를 유지하는 석출경화형 합금입니다. 어닐링 상태(O)에서는 성형성이 우수합니다. 일반 물성 항목값조건관련 표준 밀도2.8 g/cm³OAA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241 기계적 물성 항목값조건관련 표준비고 굴곡 피로 강도90.0 MPaOAA Standards 탄성 계수73.0 GPaOAA Standards, ASTM B209, ASTM B210, ASTM B
개요 AA 2014 T4는 석출경화형 알루미늄 합금으로, 열처리 후 높은 강도를 유지하면서 우수한 가공성을 제공합니다. 항공기 구조물, 트럭 프레임, 구조용 부품에 널리 적용됩니다. 일반 물성 항목값조건관련 표준 밀도2.8 g/cm³T4AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 기계적 물성 항목값조건관련 표준비고 굴곡 피로 강도140.0 MPaT4AA Standards 탄성 계수73.0 GPaT4AA Standards, ASTM B2