AA 6061 T42는 용체화 처리 후 자연 시효된 상태로, 우수한 내식성과 성형성을 겸비한 표준 등급 알루미늄 합금입니다. 양극산화 처리성이 뛰어나고 용접 및 브레이징이 용이하며, 해수 및 대기 환경에 대한 내식성이 탁월합니다. 열간 단조에도 적합합니다.
| 특성 | 값 | 조건 | 관련 표준 |
|---|---|---|---|
| 밀도 | 2.7 g/cm³ | T42 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 특성 | 값 | 조건 | 관련 표준 | 비고 |
|---|---|---|---|---|
| 탄성 계수 | 69.0 GPa | T42 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
| 평면 변형 파괴 인성 | 22.0 - 35.0 MPa·√m | - | - | 단조 6000 시리즈 알루미늄 대표값 |
| 푸아송 비 | 0.33 | - | - | 단조 6000 시리즈 알루미늄 대표값 |
| 전단 계수 | 26.0 - 26.5 GPa | - | - | 단조 6000 시리즈 알루미늄 대표값 |
| 인장 강도 | 180.0 MPa | T42 | AA Standards, ASTM B221, ASTM B241, ASTM B345 | |
| 인장 강도 | 205.0 MPa | T42 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B483 |
| 특성 | 온도 | 값 | 조건 | 관련 표준 | 비고 |
|---|---|---|---|---|---|
| 열팽창 계수 | 20 °C | 2.36×10⁻⁵ 1/K | T42 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
| 열팽창 계수 | 100 °C | 2.36×10⁻⁵ 1/K | T42 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
| 융점 | - | 580.0 - 650.0 °C | T42 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
| 비열 용량 | - | 887.0 - 963.0 J/(kg·K) | - | - | 단조 6000 시리즈 알루미늄 대표값 |
| 열전도율 | - | 155.0 - 180.0 W/(m·K) | T42 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 특성 | 값 | 조건 | 관련 표준 |
|---|---|---|---|
| 전기 전도도 | 23,000,000 - 27,000,000 S/m | T42 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 전기 저항률 | 3.7×10⁻⁸ - 4.35×10⁻⁸ Ω·m | T42 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 원소 | 함량 범위 | 조건 | 관련 표준 |
|---|---|---|---|
| 크롬 (Cr) | 0.04 - 0.35 % | T42 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 구리 (Cu) | 0.15 - 0.40 % | T42 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 철 (Fe) | 0.70 % | T42 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 마그네슘 (Mg) | 0.80 - 1.20 % | T42 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 망간 (Mn) | 0.15 % | T42 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 실리콘 (Si) | 0.40 - 0.80 % | T42 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 티타늄 (Ti) | 0.15 % | T42 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 아연 (Zn) | 0.25 % | T42 | AA Standards, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| 특성 | 평가 |
|---|---|
| 브레이징 | 상용 공정 및 방법으로 가능 |
| 내식성 | 응력 부식 균열: O, T6, T651, T652, T6510, T6511 상태에서 운전 및 실험실 시험 중 손상 없음. T4, T451, T4510, T4511 상태에서 운전 중 손상 없음, 실험실 시험에서 제한적 손상. 전반적으로 양호하며, 산업 및 해수 대기에서 무보호 사용 가능 |
| 일반 가공성 | 일반: O 상태에서 나쁨, T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511 상태에서 보통 |
| 가공성 | 일반 (상태별): O 상태에서 양호, T4, T451, T4510, T4511 상태에서 보통, T6, T651, T652, T6510, T6511 상태에서 나쁨 |
금속
AA 6061은 우수한 표면 마감과 양극 산화 처리 능력을 갖춘 쉽게 구할 수 있는 합금입니다. 용접성과 납땜성이 뛰어나며 표면 마감이 우수합니다. 해수와 대기 조건에 대한 내식성이 있습니다. 열간 단조에 적합합니다. 일반 물성 물성 값 조건 관련 표준 밀도 2.7 g/cm³ O AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 기계적 물성 물성 값 조건 관련 표준 비고
개요 AA 6061은 우수한 표면 마감과 양극 산화 처리 능력을 갖춘 널리 사용되는 알루미늄 합금입니다. 용접성과 납땜성이 뛰어나며 깨끗한 표면 마감을 제공합니다. 해수 및 대기 조건에 대한 내식성이 우수하며, 단조 가공에도 적합합니다. 물성 데이터 일반 특성 특성값조건관련 표준 밀도2.7 g/cm³T4AA 표준, ASTM B209, B210, B211, B221, B234, B241, B313, B345, B483, B547 기계적 특성 특성값조건관련 표준비고 굴곡 피로 강도95.0 MPaT4AA 표준 탄성