AA 6061은 표면 조도가 좋고 양극 산화 처리가 잘 되어 있어 쉽게 구할 수 있는 합금입니다. 해수 및 대기 조건의 부식에 대한 내성. 열간 단조에 적합합니다.
일반
| 속성 | 값 | 상태 | 관련 표준 |
|---|---|---|---|
| 밀도 | 2.7g/cm³ | T4 | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
기계
| 속성 | 값 | 상태 | 관련 표준 | 댓글 |
|---|---|---|---|---|
| 굽힘 피로 강도 | 95.0MPa | T4 | AA 표준 | |
| 탄성 계수 | 69.0GPa | T4 | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | |
| 경도, 브리넬 | 65.0 [-] | T4 | AA 표준 | |
| 평면 변형 파괴 인성 | 22.0 - 35.0 MPa·√m | 단조 6000 시리즈 알루미늄에 일반적 | ||
| 포아송 비 | 0.33 [-] | 단조 6000 시리즈 알루미늄에 일반적 | ||
| 전단 계수 | 26.0 - 26.5GPa | 단조 6000 시리즈 알루미늄에 일반적 | ||
| 인장 강도 | 180.0MPa | T4 | AA 표준, ASTM B221, ASTM B241, ASTM B345 | |
| 205.0MPa | T4 | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B483, ASTM B547 | ||
| 240.0MPa | T4 | AA 표준 |
열
| 속성 | 온도 | 값 | 상태 | 관련 표준 | 댓글 |
|---|---|---|---|---|---|
| 열팽창 계수 | 20°C | 2.36e-05 1/K | T4 | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | |
| 100°C | 2.36e-05 1/K | T4 | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | ||
| 녹는점 | 580.0 - 650.0 °C | T4 | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 | ||
| 비열용량 | 887.0 - 963.0 J/(kg·K) | 단조 6000 시리즈 알루미늄에 일반적 | |||
| 열전도율 | 155.0 - 180.0 W/(m·K) | T4 | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
전기
| 속성 | 값 | 상태 | 관련 표준 |
|---|---|---|---|
| 전기 전도도 | 23000000.0 - 27000000.0 S/m | T4 | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| 전기 저항 | 3.7e-08 - 4.35e-08 Ω·m | T4 | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
화학적 성질
| 속성 | 값 | 상태 | 관련 표준 |
|---|---|---|---|
| 크롬 | 0.04 - 0.35% | T4 | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| 구리 | 0.15 - 0.4 % | T4 | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| 철 | 0.70% | T4 | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| 마그네슘 | 0.8 - 1.2% | T4 | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| 망간 | 0.15% | T4 | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| 실리콘 | 0.4 - 0.8% | T4 | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| 티타늄 | 0.15% | T4 | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
| 아연 | 0.25% | T4 | AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B234, ASTM B241, ASTM B313, ASTM B345, ASTM B483, ASTM B547 |
기술적 속성
| 속성 | ||
|---|---|---|
| 납땜 | 일반:상업적 프로세스 및 방법으로 가능
| |
| 부식 속성 | 응력 부식 균열:작동 및 실험실 테스트 중 손상 없음(O, T6, T651, T652, T6510, T6511), 작동 중 손상 없음, 실험실 테스트 중 제한된 손상(T4, T451, T4510, T4511), 일반:양호, 없음 산업 또는 해수 대기에서의 보호
| |
| 일반 가공성 | 일반:나쁨(O), 충분(T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511)
| |
| 작업성 | 일반(상태):양호(O), 양호(T4, T451, T4510, T4511), 불량(T6, T651, T652, T6510, T6511)
| |
금속
알루미늄 합금 AA 2219, 시효 경화성 합금은 구리 첨가제로 생산됩니다. 우수한 구조적 강도로 잘 알려져 있으며 수많은 고온 응용 분야에 사용됩니다. 기계가공, 성형, 열처리, 냉간가공 등 많은 금속가공 공정에 적합한 합금입니다. 속성 일반 속성 값 상태 관련 표준 밀도 2.84g/cm³ 오 AA 표준, ASTM B209, ASTM B221, ASTM B241 기계 속성 값 상태 관련 표준 댓글 탄성 계수 73.0GPa 오 AA 표준, ASTM B
AA 6061은 표면 조도가 좋고 양극 산화 처리가 잘 되어 있어 쉽게 구할 수 있는 합금입니다. 해수 및 대기 조건의 부식에 대한 내성. 열간 단조에 적합합니다. 속성 일반 속성 값 상태 관련 표준 밀도 2.7g/cm³ 오 AA 표준, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B345, ASTM B483 기계 속성 값 상태 관련 표준 댓글 굽힘 피로 강도 60.0MPa