Harada C5191HQ is a high-quality phosphor bronze developed to meet the growing demand for higher strength and superior bendability in miniaturized electronic components. The alloy is specifically designed for hot-dip tin plating, ensuring excellent solderability and corrosion protection for connector and terminal applications.
| Property | Value |
|---|---|
| Density (Relative) | 8.82 g/cm³ |
| Property | H Temper | EH Temper | SH Temper |
|---|---|---|---|
| Tensile Strength (Rm) | 630 MPa | 699 MPa | 744 MPa |
| Yield Strength (Rp0.2) | 614 MPa | 697 MPa | 739 MPa |
| Elongation (A) | 22.6 % | 13.7 % | 12.7 % |
| Vickers Hardness (HV) | 203 | 214 | 222 |
| Bendability 90° (Good Way) | 0 × t | 0 × t | 1 × t |
| Bendability 90° (Bad Way) | 0 × t | 0 × t | 1 × t |
| Elastic Modulus (E) | 115 GPa | ||
| Flexural Modulus | 105 GPa | ||
| Property | Value |
|---|---|
| Coefficient of Thermal Expansion | 18.2 × 10⁻⁶ /K |
| Melting Range | 900 – 1040 °C |
| Specific Heat Capacity | 375 J/(kg·K) |
| Thermal Conductivity | 67 W/(m·K) |
| Property | Value |
|---|---|
| Electrical Conductivity (IACS) | 14 % |
| Element | Content | Note |
|---|---|---|
| Copper (Cu) + Tin (Sn) + Phosphorus (P) | 99.8 min | Balance |
| Tin (Sn) | 5.5 – 7.0 | |
| Phosphorus (P) | 0.03 – 0.20 | |
| Iron (Fe) | 0.01 max | |
| Lead (Pb) | 0.01 max | |
| Zinc (Zn) | 0.01 max |
| Parameter | Standard Range |
|---|---|
| Base Material Thickness | 0.1 – 0.8 mm |
| Plating Thickness (per side) | 0.7 – 8.0 µm |
| Strip Width (after slitting) | 8.0 – 170 mm |
| Coil Unit Weight | 1.0 / 2.0 / 4.0 / 8.0 kg/mm |
| Coil Inner Diameter | 250 / 300 / 400 / 500 mm |
| Plating Material | Pure Tin (Sn) |
| Base Material | Phosphor Bronze (C5191HQ) |
Notes: Width refers to slit width after plating. Differential plating thickness per side available. Custom specifications welcome – contact us.
| Thickness Range | Harada Internal Spec | JIS Standard (H3110, H3130) |
|---|---|---|
| 0.05 – 0.08 mm | ±0.002 mm | ±0.005 mm |
| 0.09 – 0.15 mm | ±0.002 mm | ±0.008 mm |
| 0.16 – 0.25 mm | ±0.003 mm | ±0.013 mm |
| 0.26 – 0.30 mm | ±0.004 mm | ±0.018 mm |
Harada's internal tolerances are significantly tighter than JIS standards.
Contact the supplier for specific requests regarding chemical composition, mechanical properties, or thickness.
금속
개요 UGIMA® 4104는 UGITECH에서만 생산되는 가공성 개선형 페라이트계 스테인리스강입니다. 기본 특성은 UGI 4104와 동일하지만, UGIMA® 공법(개재물 제어 기술)을 적용하여 가공성을 획기적으로 향상시켰습니다. 주요 특징 UGIMA® 공법으로 개재물 분포를 최적화하여 어떤 가공 조건, 공작기계, 공구를 사용하더라도 뛰어난 성능 발휘 풀림 상태 선삭 가공 시 UGI 4104 대비 생산성 4% 향상 열처리 상태 선삭 가공 시 생산성 25% 향상 풀림 상태에서 Ø4mm HSS 드릴 가공 시 생산성 최대
개요 UGIMA® 4542는 UGIMA® 계열의 첫 번째 침탄경화형(석출경화형) 스테인리스강으로, UGITECH에서만 생산됩니다. 기본 특성은 UGI 4542와 동일하나, 가공성이 현저히 우수합니다. 주요 특징 UGIMA® 신기술로 1.4542 강종 대비 현저한 이점 제공 UGI 4542 대비 생산성 20~30% 향상 오스테나이트강 1.4301/1.4307(304/304L) 수준의 우수한 내식성 열처리 조건에 따라 다양한 기계적 특성 구현 가능 (고인장강도 ~ 고충격강도) 미세 조직 마르텐사이트 기지에 일부 페